混合无名称 |
混合比 |
折射率 |
透光区域 |
蒸发温度 |
蒸发源 |
应用 |
|
|
ZrO2/TiO2 |
90:10 |
2.0/550nm |
400～7000 |
2300℃ |
W E |
AR coatings |
|
|
50:50 |
2.05-2.15 |
400～7000 |
|
|
ZrO2/Ta2O5 |
70:30 |
2.1/550nm |
400～7000 |
2300～2500℃ |
W E |
AR coatings |
|
|
|
TiO2/Ta2O5 |
70:30 |
2.25～2.3 |
400～7000 |
2200℃ |
E |
AR coatings |
|
|
80:20 |
|
|
50:50 |
|
|
Al2O3/MgO |
50:50 |
1.65～1.7 |
200～5000 |
2000℃ |
E |
UV coatings |
|
|
at 500nm |
|
|
ZrO2/Al2O3 |
40:60 |
1.7/550nm |
250～5000 |
1500℃ |
E |
AR coatings |
|
|
|
La2O3/Al2O3 |
50:50 |
1.7/500nm |
400～7000 |
1900～2000℃ |
E |
AR coatings |
|
|
70:30 |
1.8/500nm |
Mutilayers |
|
|
In2O3/SnO2 |
90:10 |
2.0/500nm |
400～8000 |
1560℃ |
E Al2O3 |
Conductive |
|
|
95:5 |
|
|
5:95 |
|
|
La2O3/TiO2 |
|
2.0/500nm |
400～7000 |
2100~2200℃ |
E Mo |
AR Multi-layers |
|
|
TiO2/Nb2O5 |
|
2.0/501nm |
400～7000 |
2300~2500℃ |
E M |
Multi-layers |
| |
|
| |
|
|
|
|